HTS-4111 is a modified cycloaliphatic amine based epoxy curing agent with low viscosity and light colour. It is widely used with stable colour, high gloss, hardness and good flexibility on civil engineering top coating (flooring), high solids primer and lining coating for pipelines and storage tanks with good corrosion and chemical resistance. When properly formulated, good adhesive, synthetic flooring and potting properties are observed.
Technical properties:
Appearance: Colourless to light yellow liquid
Viscosity (25°C, mPa.s ): 200-400
Colour (Gardner): ≦ 3
Density (25°C, g/ml): 1.01-1.02
AHEW (g/eq): 112-114
Ratio with E51 epoxy resins (EEW~190) 100/58-62
HTS-4111 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4112
HTS-4112 is a modified cycloaliphatic amine based epoxy curing agent with low viscosity and light colour. It can effectively prevent the amine brush on the coating surface under humid conditions. It is widely used with stable colour, high gloss, hardness and good flexibility on civil engineering top coating (flooring), good corrosion and chemical resistance on metal coating When properly formulated, good adhesive, synthetic flooring and potting properties are observed.
Technical properties:
Appearance: Colourless to light yellow liquid
Viscosity (25°C, mPa.s ): 1100-1600
Colour (Gardner): ≦ 3
Density (25°C, g/ml): 1.01-1.02
AHEW (g/eq): 118-120
Ratio with E51 epoxy resins (EEW~190) 100/60-62
HTS-4112 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4512
HTS-4512 is a modified aliphatic amine based epoxy curing agent with low viscosity and light colour. It is widely used with fast curing and good corrosion chemical resistance. When properly formulated, low temperature/fast curing adhesive, the coating/glue for traffic marks and potting properties are observed.
Technical properties:
Appearance: Colourless to light yellow liquid
Viscosity (25°C, mPa.s ): 240-260
Colour (Gardner): ≦ 2
Density (25°C, g/ml): 0.97-1.00
AHEW (g/eq): 25-26
Ratio with E51 epoxy resins (EEW~190) 100/13-14
HTS-4512 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4514
HTS-4514 is a modified Mannich base (without free phenol) epoxy curing agent. It provides fast setting, low-temperature curing (5-10°C), chemically resistant, high solids sprayable coating with good corrosion resistance similar to conventional polyamides. When properly formulated, good adhesive, synthetic flooring and potting properties are observed.
It has variable advantages featuring as below:
1. Low viscosity,
2. Light colour,
3. Low temperature curing,
4. Excellent moisture resistance,
5. Phenol free containing,
6. High gloss, blush-free surface.
Based on these, it is very suitable to be used in:
1. Chemical resistant coating, tank linings,
2. High solids and solvent free coatings,
3. Synthetic flooring,
4. Accelerator or co-curing agent for polyamides
5. Structural adhesives,
6. Potting, casting and encapsulation
Technical properties:
Amine value: 350-390
Viscosity (25°C, mPa.s ): 400-700
Colour (Gardner): ≦ 5
Density (25°C, g/ml): 0.99-1.01
AHEW (g/eq): 76-78
HTS-4514 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/drum
HTS-4515
HTS-4515 is a modified Mannich base (without free phenol) epoxy curing agent. It provides fast setting, low-temperature curing. It is used in particular for accelerating the curing with polyamides as the main curing agents. When properly formulated, good adhesives for metal and plastics are observed.
Technical properties:
Appearance: Amber liquid
Viscosity (25°C, mPa.s ): 110-160
Colour (Gardner): < 16
Density (25°C, g/ml): 1.06-1.07
AHEW (g/eq): 38-40
Ratio with E51 epoxy resins 100/20
HTS-4515 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4516
HTS-4516 is a modified aliphatic amine base epoxy curing agent with excellent thermal resistance. It provides fast setting, high HDT and fast curing. It is widely used in particular for accelerating the curing with amido-amine and/or polyamides as the main curing agents. When properly formulated, good adhesives for metal and plastics and also top flooring coating under low temperature are observed.
Technical properties:
Appearance: Light yellow liquid
Viscosity (25°C, mPa.s ): 100-200
Colour (Gardner): < 6
Density (25°C, g/ml): 1.01-1.02
AHEW (g/eq): 34-36
Ratio with E51 epoxy resins 100/18
HTS-4516 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4517
HTS-4517 is a modified aliphatic amine base epoxy curing agent tailored for HTM-5102 & HTM-5103 as epoxy resins in the formulations. It provides fast curing, high solid coating and low temperature curing. It is widely used in particular for thin coating film and fast adhesives When properly formulated, good fast resin casting and mould gel coat are also observed.
Technical properties:
Appearance: Light yellow liquid
Viscosity (25°C, mPa.s ): 1200-1800
Colour (Gardner): < 6
Density (25°C, g/ml): 0.97-0.98
AHEW (g/eq): 90-95
Ratio with E51 epoxy resins 100/47-50
Ratio with HTM-5102 epoxy resins 100/60-65
Ratio with HTM-5103 epoxy resins 100/60-65
HTS-4517 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4518
HTS-4518 is a modified aliphatic amine based epoxy curing agent with low viscosity, colour and moderate reactivity. It can effectively prevent the amine brush on the coating surface under humid conditions. It is widely used with stable colour, high gloss and good flexibility on civil engineering top coating (flooring) at all seasons. It can also be used with other darker curing agents to improve the appearance of the coating and prolonged pot life. When properly formulated, high gloss thicker coating, good adhesive for , synthetic flooring and electronic encapsulation are observed.
Technical properties:
Appearance: Colourless to light yellow liquid
Viscosity (25°C, mPa.s ): 45-65
Colour (Gardner): ≦ 3
Density (25°C, g/ml): 0.94-0.95
AHEW (g/eq): 76-78
Ratio with E51 epoxy resins (EEW~190) 100/40
HTS-4518 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4519
HTS-4519 is a modified aliphatic amine based epoxy curing agent with moderate viscosity but fast curing. It can be used with liquid epoxy resins in the presence of reactive diluents to make chemical resistant coating, casting, gel coat and laminating adhesives.
Technical properties:
Appearance: Yellow liquid
Viscosity (25°C, mPa.s ): 3000-5000
Colour (Gardner): < 9
Density (25°C, g/ml): 1.06-1.08
AHEW (g/eq): 38-40
Ratio with E51 epoxy resins (EEW~190) 100/20
HTS-4519 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4520
HTS-4520 is a modified aliphatic amine based epoxy curing agent with low viscosity and light colour. It is widely used with high reactivity, hardness and low shrinkage to make adhesives, electrical casting and putty for panel beating.
Technical properties:
Appearance: Light yellow liquid
Viscosity (25°C, mPa.s ): 50-350
Colour (Gardner): <4
Density (25°C, g/ml): 1.02-1.04
AHEW (g/eq): 48-50
Ratio with E51 epoxy resins (EEW~190) 100/25
HTS-4520 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4521
HTS-4521 is a modified aliphatic amine base epoxy curing agent with low viscosity. It is widely used to make coatings for brushes, laminates, electrical casting and high solid protective coating. The ratio to epoxy resins is not very critical to have the final products with high insulation properties, even at room or elevated temperature. Specifically it could be diluted by water to be the curing agent for waterbased adhesives.
Technical properties:
Appearance: Light yellow liquid
Viscosity (25°C, mPa.s ): 125-210
Colour (Gardner): < 3
Density (25°C, g/ml): 0.99-1.00
AHEW (g/eq): 45-47
Ratio with E51 epoxy resins 100/24
HTS-4521 should be kept in tightly closed original container in a dry, cool place without direct sunlight. In this case the storage shelf life is at least two years from the manufacturing date.
Package: 200kg/steel drum
HTS-4522
HTS-4522 is a modified aliphatic amine based epoxy curing agent with low viscosity and light colour. It can be used with liquid epoxy resins to make industrial coating, adhesives and protective film on plastic surface at room temperature.
HTS-4531
HTS-4531 is a modified aliphatic amine base epoxy curing agent with excellent thermal resistance. It provides fast setting, high HDT and fast curing. When properly formulated, good adhesives for metal and plastics and also top flooring coating under low temperature are observed.
HTS-4543
HTS-4543 is a modified aliphatic amine based epoxy curing agent with moderate viscosity and light colour. It is widely used with high reactivity, hardness and low shrinkage to make adhesives, electrical casting and putty for panel beating.
HTS-4548
HTS-4548 is a modified amine based epoxy curing agent with low viscosity. It can be used to get excellent flexibility and adhesion. With properly formulations, good chemical resistance, adhesions, mechanical impact resistance and electrical insulation properties can be achieved.
HTS-4701
HTS-4701 is a modified aliphatic amine based epoxy curing agent with low viscosity, low colour and moderate reactivity. It can be used to get excellent chemical/solvent, corrosion resistance, good hardness and mechanical impact resistance.